3D Printing of highly textured bulk thermoelectric materials: Mechanically robust BiSbTe alloys with superior performance

Junhao Qiu, Yonggao Yan*, Tingting Luo, Kechen Tang, Lei Yao, Jian Zhang, Min Zhang, Xianli Su, Gangjian Tan, Hongyao Xie, Mercouri G. Kanatzidis, Ctirad Uher, Xinfeng Tang

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

119 Scopus citations


While zone-melted (ZM) Bi2Te3 is a standard commercially available thermoelectric (TE) material, it suffers from not being sufficiently mechanically robust due to the presence of the van der Waals bonded Te-Te layers that reduce the product yield and compromise operational reliability. Polycrystalline materials prepared by powder metallurgy techniques exhibit improved mechanical properties but usually lose the desired texture exhibited by ZM ingots, and this affects their TE performance. It is highly desirable to be able to fabricate Bi2Te3-based bulk materials with anisotropies similar to a single crystal, yet being mechanically strong as the polycrystalline specimens. Herein, we combine for the first time the thermal explosion technique with selective laser melting (SLM) to synthesize the highly textured p-type Bi0.4Sb1.6Te3 bulk material. Structural analysis (FESEM and XRD) indicates that the slender columnar grains grew along the building direction (BD) of the structure and the orientation factor reached up to 0.9, close to that representing a single crystal. TEM images revealed a high density of dislocations inside the grains. Since the printed compound has a high degree of texture, the TE and mechanical properties exhibit a highly anisotropic behavior. The maximum ZT of annealed samples parallel to the BD was 1.1, similar to that of the single crystal. However, the compressive strength of the structure reached up to 91 MPa, some 2.5 times the strength of a typical single crystal (37 MPa), and even higher than that of Spark Plasma Sintered (SPS) polycrystalline samples (80 MPa). Meanwhile, the mechanical cutting performance was much superior compared to that of the ZM ingot, and TE legs could be cut to sizes as small as 0.2 mm. A micro-TE module assembled using SLM-printed high performance p-type BiSbTe and SPS-compacted n-type BiTeSe materials showed the maximum cooling temperature difference of 62 °C. The work provides a facile and effective solution for preparation of Bi2Te3-based materials with high texture, robust mechanical properties, and excellent TE performance. As such, it lays a solid foundation for rapid in situ 3D printing of Bi2Te3-based micro-TE devices.

Original languageEnglish (US)
Pages (from-to)3106-3117
Number of pages12
JournalEnergy and Environmental Science
Issue number10
StatePublished - Oct 2019

ASJC Scopus subject areas

  • Environmental Chemistry
  • Renewable Energy, Sustainability and the Environment
  • Nuclear Energy and Engineering
  • Pollution


Dive into the research topics of '3D Printing of highly textured bulk thermoelectric materials: Mechanically robust BiSbTe alloys with superior performance'. Together they form a unique fingerprint.

Cite this