Fe-substituted SrTiO3-δ-Ce0.9Gd 0.1O2 composite anodes for solid oxide fuel cells

Sungmee Cho, Daniel E. Fowler, Elizabeth C. Miller, J. Scott Cronin, Kenneth R. Poeppelmeier, Scott A. Barnett*

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

67 Scopus citations


A new composite solid oxide fuel cell anode material, SrTi 1-xFexO3-δ mixed with Gd-doped ceria, was tested in La0.9Sr0.1Ga0.8Mg 0.2O3-δ electrolyte-supported cells with La 0.4Ce0.6O2 barrier layers and La 0.6Sr0.4Fe0.8Co0.2O3 cathodes. The x = 0.7 composition had an anode polarization resistance of 0.17 Ω cm2, at 800 °C in humidified H2, much lower than the value 0.39 Ω cm2 measured for x = 0.4 and 3.14 Ω cm2 for x = 0. The reduced polarization resistance correlated with increased oxygen non-stoichiometry δ, which suggests that it may be related to increased ionic conductivity. Electrochemical impedance spectroscopy (EIS) measurements at 800 °C on the x = 0.7 anode cell showed a main response centered at ∼1 Hz that increased with decreasing hydrogen partial pressure. The maximum power density observed was for the x = 0.7 cell-337 mW cm-2 at 800 °C in air and humidified hydrogen-and was limited mainly by the thick electrolyte.

Original languageEnglish (US)
Pages (from-to)1850-1857
Number of pages8
JournalEnergy and Environmental Science
Issue number6
StatePublished - Jun 2013

ASJC Scopus subject areas

  • Environmental Chemistry
  • Renewable Energy, Sustainability and the Environment
  • Nuclear Energy and Engineering
  • Pollution


Dive into the research topics of 'Fe-substituted SrTiO<sub>3-δ</sub>-Ce<sub>0.9</sub>Gd <sub>0.1</sub>O<sub>2</sub> composite anodes for solid oxide fuel cells'. Together they form a unique fingerprint.

Cite this