Stable high current density operation of La0.6Sr0.4Co0.2Fe0.8O3-: δ oxygen electrodes

Matthew Y. Lu, Justin G. Railsback, Hongqian Wang, Qinyuan Liu, Yvonne A. Chart, Shan Lin Zhang, Scott A Barnett*

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

6 Scopus citations

Abstract

Solid oxide cells operated reversibly between fuel cell and electrolysis modes are promising for energy storage with extremely high capacity. La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF) has become the dominant oxygen electrode material in electrolysis and reversible operation. However, LSCF has been widely reported to degrade due to Sr surface segregation. The present understanding is that the segregation rate and hence the degradation rate increases with increasing temperature and current density. Here we present a study of LSCF electrode performance and stability carried out with a series of extended life tests (1000 hours) over a range of temperatures and reversing current densities. Although the results at lower temperatures (650-700 °C) show the expected increase in segregation-induced degradation with increasing current density, at higher temperature (750 °C) stability is improved and the electrodes become fully stable at the highest current density of 1.5 A cm-2, maintaining a stable polarization resistance of 0.08 Ω cm2. This unexpected result is explained by the increased electrochemical activity of LSCF at the higher temperature and a very rapid development of a stable surface segregated Sr layer.

Original languageEnglish (US)
Pages (from-to)13531-13539
Number of pages9
JournalJournal of Materials Chemistry A
Volume7
Issue number22
DOIs
StatePublished - Jan 1 2019

ASJC Scopus subject areas

  • Chemistry(all)
  • Renewable Energy, Sustainability and the Environment
  • Materials Science(all)

Fingerprint Dive into the research topics of 'Stable high current density operation of La<sub>0.6</sub>Sr<sub>0.4</sub>Co<sub>0.2</sub>Fe<sub>0.8</sub>O<sub>3-: δ</sub> oxygen electrodes'. Together they form a unique fingerprint.

Cite this